C; C-carbon foam; thermal insulation; shear strength; composites
This paper was focused on the development of a new composite for high thermal insulation applications with carbon/carbon (C/C) composites, carbon foams and an interlayer of phenolic-based carbon. The microstructure, mechanical properties, fracture mechanism and thermal insulation performance of the composite was investigated. The experiment results showed that the bonding strength of the C/C-carbon foam composite was 4.31 MPa, and that the fracture occurred and propagated near the interface of the carbon foam and the phenolic-based carbon interlayer due to the relatively weak bonding. The shear load-displacement curves were characterized by alternated linear slopes and serrated plateaus before a final failure. he experiment revealed that the thermal conductivity of the C/C-carbon foam composite was 1.55 W center dot m(-1)cK(-1) in 800celcius, which was 95.8% lower than that of C/C composites, proving that the thermal insulation of the new foam composite was greatly enhanced by the carbon foam with its porous hollow microstructure.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据