期刊
SCRIPTA MATERIALIA
卷 162, 期 -, 页码 38-43出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.scriptamat.2018.10.033
关键词
Al0.5CrFeNiCo; Friction stir processing; Al3Ni; Strength; Ductility
类别
资金
- Army Research Laboratory [W911NF-16-2-0189]
- University of North Texas [W911NF-16-2-0189]
Modification of a coarse B2 phase and realization of hierarchical multi-phase microstructures were achieved in an Al0.5CrFeCoNi complex concentrated alloy (CCA) using high-temperature severe plastic deformation (HTSPD). Under HTSPD conditions, a thermodynamically stable B2 phase dissolved, while a thermodynamically unstable coarse Al3Ni phase formed. Al supersaturation in the matrix after HTSPD led to the formation of fine B2 precipitates during the subsequent aging treatment. The combination of Al3Ni for enhanced work hardening and fine B2 precipitates for strength resulted in excellent strength-ductility of 1400 MPa and 20%. (C) 2018 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据