In this study, highly porous activated carbon was produced from rice straw by carbonization and followed by activation using potassium hydroxide (KOH). Activated carbon samples were prepared under different activation temperatures, i.e., 650, 750 and 850 degrees C, and their physical and chemical properties were characterized accordingly. The BET surface area of the activated carbon samples was increased from 520 to 1048 m(2)/g with the increase of activation temperature from 650 to 850 degrees C. These values were much higher than the non-activated rice straw carbon i.e., 1.16 m(2)/g. The pore sizes of the rice straw activated carbon were found to be mainly in mesopore size range of 2-50 nm. Total carbon content of the AC sample was increased from 8.35% to 31.73% with the increase of activation temperature from 650 to 850 degrees C. XRD and Raman spectroscopy confirmed the graphite properties of the activated carbons produced. SEM images proved high porosity of the AC after KOH activation.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据