DOI: 10.1016/j.msea.2018.12.123
关键词
Bulk metallic glasses; Glass-forming ability; Thermal stability; Mechanical properties
类别
资金
- NSFC [51671166/51827801/51434008]
In this work, the effects of Ag substitution for Ti in Zr56Cu24Al9Ni7Ti4-xAgx (x = 0, 1, 2, 3, and 4 at%) bulk metallic glasses (BMGs) on the glass-forming ability, thermal stability and mechanical properties are investigated. The present research shows that the critical diameter increases to 6-8 mm for Ag content of x = 2 and 3 at%. Additionally, with increasing in the content of Ag, with a rod diameter of 3 mm, the glass-forming ability and thermal stability were effectively improved. The largest ultimate fracture strength and plastic strain were observed for alloys where x = 2 with a rod diameter in 3 mm (1863 (+/- 25) MPa and 7.9 (+/- 0.6) %, respectively). Different fracture modes were observed using scan electron microscopy after compressive testing. This work illustrates that Ag can play an important role in improving glass-forming ability, thermal stability and mechanical properties for amorphous alloys.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据