期刊
JOURNAL OF MATERIALS SCIENCE-MATERIALS IN ELECTRONICS
卷 30, 期 5, 页码 4519-4526出版社
SPRINGER
DOI: 10.1007/s10854-019-00740-3
关键词
-
类别
资金
- National Natural Science Foundation [11604097]
- Fund of East China University of Science and Technology [YK0142119]
- Natural Science Foundation of Jiangsu Province [BK20141167]
Ternary compound Cu2SnS3 (CTS) was fabricated by simple, low cost and high efficient spray pyrolysis and rapid thermal annealing route. The influences of annealing temperature and annealing duration on the properties of the prepared CTS thin film were investigated in detail. X-ray diffraction spectrometer, Scanning Electron Microscope, UV-Vis-IR spectrophotometer and I-V test system were employed for the analysis of the structural, morphological, optical and photoelectric properties of the prepared CTS thin film, respectively. The characterization results show that the CTS thin film prepared under the optimal annealing condition of 500 degrees C and 15min presents as tetragonal structure with preferential (1,1,2), bandgap value of 1.44eV, crystal grain size of around 80nm and photoelectric conversion efficiency as high as 1.24%.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据