JOURNAL OF MATERIALS SCIENCE-MATERIALS IN ELECTRONICS
卷 30, 期 7, 页码 6660-6668出版社
SPRINGER
DOI: 10.1007/s10854-019-00975-0
关键词
-
类别
资金
- Mexican National Council for Science and Technology (CONACYT) [CB-254903]
- PRODEP [UAEH-PTC-801, 511-6/18-8661]
The present work focuses on the deposition of ZnO thin films on crystalline and porous Germanium substrates for hazardous gas detection. The porous Ge substrates were obtained by means of surface exfoliation by using H+ implantation and subsequent annealing. Morphological analysis revealed the formation of pores in the range between 1 and 5 mu m. The deposition of ZnO thin films has been made on crystalline and porous Ge substrates utilizing the dip coating method. Structural and morphological characterizations confirmed the formation of highly porous polycrystalline ZnO film exclusively on porous Ge substrates. All the obtained samples were tested for their sensitivities at 0.1, 0.5, 1 and 2% of CO2 concentrations. The ZnO films deposited on porous Ge exhibited an increment of sensing response by a factor of 2, which is correlated to the increment of the superficial area induced by the substrate. Maximum sensing response similar to 50% was achieved for 2% of CO2 when measured at 300 degrees C. ZnO over porous Ge films showed complete resistance recovery, whereas ZnO over crystalline Ge showed a drift in the recovery resistance. ZnO deposited porous Ge showed the fastest response and recovery time similar to 25 and 10s, respectively.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据