关键词
Phosphate glass fibers; Strength; Fatigue; Elastic modulus
资金
- Politecnico di Torino through the Interdepartmental Centre PhotoNext
Calcium-phosphate glass optical fiber and capillaries (with composition identical to the core and the cladding of the fiber) were fabricated and subjected to mechanical characterization. Tensile tests were carried out to determine the strength distribution, the fatigue behavior and the elastic modulus of fibers and capillaries. The tests were performed without the application of any coating, in order to assess the behavior in bare conditions, just like in the provisional application as bio-resorbable elements. Strength ranging from 200 to 350 MPa was measured for both fiber and capillaries, the Weibull's modulus being around 3 to 6, thus revealing quite scattered distributions associated to the presence of variable surface flaws. The elastic modulus of the two glasses was shown to depend on the specific composition, the presence of MgO being responsible for a stiffer material. An evident sub-critical crack growth was also pointed out in the presence of water. (C) 2018 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据