EUROPEAN POLYMER JOURNAL
卷 112, 期 -, 页码 334-345出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.eurpolymj.2018.12.035
关键词
Cellulose nanocrystal; Methylcellulose; Nanocomposite fiber; Liquid crystal; Toughness
资金
- ERC
- Tekniikan Edistamissaatio (The Finnish Foundation for Technology Promotion)
Methylcellulose/cellulose nanocrystal (MC/CNC) nanocomposite fibers showing high ductility and high modulus of toughness were prepared by a simple aqueous wet-spinning from corresponding nanocomposite hydrogels into ethanol coagulation bath followed by drying. The hydrogel MC aq. concentration was maintained at 1 wt-% while the CNC aq. loading was systematically varied in the range 0-3 wt-%. This approach resulted in MC/CNC fiber compositions from 25/75 wt-%/wt-% to 95/5 wt-%/wt-%. The optimal mechanical properties were achieved with the MC/CNC composition of 80/20 wt-%/wt-% allowing high strain (36.1%) and modulus of toughness (48.3 MJ/m(3)), still keeping a high strength (190 MPa). Further, we demonstrate that the continuous spinning of MC/CNC fibers is potentially possible. The results indicate possibilities to spin MC-based highly ductile composite fibers from environmentally benign aqueous solvents.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据