期刊
ELECTROCHIMICA ACTA
卷 295, 期 -, 页码 778-786出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.electacta.2018.11.009
关键词
Lithium-ion battery; Silicon composite electrode; Partial lithiation; Degradation; Cycling
资金
- National Natural Science Foundation of China [11332005, 11702166]
Partial lithiation strategies for silicon composite electrodes are experimentally investigated in this article. Two types of partial lithiation, i.e. voltage- and capacity-control strategies, are presented. Capacity loss and irreversibility of silicon electrodes are significantly suppressed by either partial lithiation strategy without any complicated modifications or treatments. The capacity of partially lithiated silicon electrodes is even higher than that of fully lithiated one after certain cycles. The images of scanning electron microscope suggest that the mechanical damage generated in partially lithiated electrodes is less than that in fully lithiated one. Furthermore, after dozens of cycles with partial lithiation, capacity decay also slows down in subsequent full charge-discharge cycles. The presented experimental results suggest that the partial lithiation strategy relieves the coupled mechanical-electrochemical degradation and is a promising approach for the long-term use of silicon composite electrodes. (C) 2018 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据