CONSTRUCTION AND BUILDING MATERIALS
卷 198, 期 -, 页码 479-493出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.conbuildmat.2018.11.197
关键词
Extrudable foamed concrete; Lightweight foamed concrete; Fiber reinforced concrete; GFRP mesh; Polymer fibers; Curing conditions; Dry density
An extensive experimental campaign was carried out to investigate the mechanical strength of fiber-reinforced lightweight foamed concrete. The considered foamed concrete was prepared with a viscosity enhancing agent that increases the cohesion and consistency of the cement paste at the fresh state (extrudable foamed concrete). The flexural strength was evaluated on almost 60 small-scale prismatic beam specimens, and the compressive strength on 100 cubic specimens in accordance with two different testing standards for comparative purposes. The effects of three different curing conditions (air, cellophane and water), three target dry densities (400, 600, 800 kg/m(3)), three fiber contents (0.7%, 2.0%, 5.0%), and the presence of an additional glass-fiber-reinforced-polymer (GFRP) mesh in the tensile zone of the beams (besides the short fibers) were analyzed. The polymer fibers increased the flexural capacity of the beams, especially for the low-density specimens and for the higher contents of fibers (2.0% and, above all, 5.0%), but had a negligible influence on the compressive strength. The additional GFRP mesh combined with the short fibers improved the flexural capacity considerably in all the examined conditions, turning out to be the best strategy for obtaining high mechanical strengths associated with low densities typical of ultra-lightweight concrete elements. (C) 2018 The Author(s). Published by Elsevier Ltd.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据