期刊
CERAMICS INTERNATIONAL
卷 45, 期 9, 页码 11625-11632出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.ceramint.2019.03.034
关键词
Sintering temperature; Sintering time; Mechanical property; Dielectric; Microwave absorption
资金
- National Natural Science Foundation of China, China [51072165, 51402239]
- Fundamental Research Funds for the Central Universities [3102014JCY01002]
Silicon carbide fiber-reinforced mullite matrix (SiCf/Mu) composites were fabricated via an infiltration and sintering method. Effects of sintering parameters on microstructure, mechanical, dielectric and microwave absorption properties of SiCf/Mu composites have been investigated. The flexural strength is significantly improved with increasing sintering temperature, and the highest flexural strength of 213 MPa is obtained in vacuum at 1000 degrees C for 2 h. The performances of composites with different holding time are further studied at 1000 degrees C. The flexural strengths of composites sintered at 1000 degrees C for 2 and 4 h reach 213 and 219 MPa, respectively. The failure displacement of the composite sintered at 1000 degrees C for 4 h reaches 0.39 mm. The excellent microwave absorption properties are achieved for the composite sintered at 1000 degrees C for 2 h. The minimum reflection loss (RL) reaches -38 dB with a thickness of 2.9 mm at 12 GHz and the effective absorbing bandwidth (RL <= -10 dB) with a thickness of 3.4 mm covers the whole X - band, which indicate that SiCf/Mu composite is a good candidate for microwave absorbing materials. These results provide valuable solutions to obtaining structural-functional materials for microwave absorption applications in civil and military areas.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据