期刊
CERAMICS INTERNATIONAL
卷 45, 期 3, 页码 3217-3222出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.ceramint.2018.10.224
关键词
Y2O3 transparent ceramics; Sintering additives; Optical transmittance; Spectroscopic properties
资金
- Romanian National Authority for Scientific Research and Innovation through the program NUCLEU [LAPLAS V 3N/2018]
- Laserlab-Europe EU-H2020 [654148]
(Y0.87-xLa0.1Zr0.03Ybx)(2)O-3 (x = 0.02, 0.04, 0.05) transparent ceramics were obtained by solid-state reaction and combined sintering procedures with La2O3 and ZrO2 as sintering additives. A method based on two-step intermediate sintering in air followed by vacuum sintering was applied in order to control the densification and grain growth of the samples during the final sintering process. The results indicate that La2O3 and ZrO2 co-additives can improve the microstructure and optical properties of Yb:Y2O3 ceramics at relatively low sintering temperature. On the other hand, the addition of Zr4+ ions leads to the formation of dispersed scattering volumes in the ceramic bodies. Transmittance of 78.8% was measured for the 2.0 at% Yb:Y2O3 ceramic sample at the wavelength of 1100 nm. The spectroscopic properties of Yb:Y2O3 ceramics were investigated at room temperature. The obtained results show that the absorption cross-section at 978 nm is in the range of 2.08 x 10(-20) to 2.36 x 10(-20) cm(2), whereas the emission cross-section at 1032 nm is similar to 1.0 x 10(-20) cm(2).
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据