期刊
CATALYSIS TODAY
卷 339, 期 -, 页码 200-209出版社
ELSEVIER
DOI: 10.1016/j.cattod.2019.01.071
关键词
Three-dimensionally ordered macropore; Ceria; Chromia; Chromiaceria composite oxide; Trichloroethylene oxidation
资金
- NSF of China [21677004]
- National High Technology Research and Development Program (863 Program) of China [2015 AA034603]
Three-dimensionally ordered macroporous (3DOM) CeO2, 3DOM Cr2O3, 3DOM xCr(2)O(3)-CeO2(x (the weight percentage of Cr2O3) = 3.5, 5.5, and 8.0 wt%), and 5.5 wt% Cr2O3/3DOM CeO2 samples were prepared using the polymethyl methacrylate (PMMA)-templating and incipient wetness impregnation methods, respectively. A number of techniques were used to characterize physicochemical properties of the materials, and their catalytic activities were evaluated for the oxidation of trichloroethylene (TCE). These samples possessed a good-quality 3DOM structure and a surface area of 35 - 47 m(2)/g. The 3DOM 5.5Cr(2)O(3)-CeO(2 )sample performed the best (the temperature at TCE conversion = 90% = 255 degrees C at a space velocity of 20,000 mL/(g h)). Effects of water vapor and carbon dioxide on activity of the 5.5Cr(2)O(3)-CeO2 sample were also examined. It is observed that partial deactivation induced by H2O introduction of the 5.5Cr(2)O(3)-CeO2 sample was reversible, while that induced by CO2 addition was irreversible. Based on the activity data and characterization results, it is concluded that the good catalytic activity and thermal stability of 3DOM 5.5Cr(2)O(-)CeO(2) was associated with its high adsorbed oxygen species concentration, good low-temperature reducibility, and strong interaction between Cr2O3 and CeO2. We believe that the 3DOM 5.5Cr(2)O(3)-CeO2 catalyst is promising in the application for oxidative removal of chlorinated volatile organic compounds.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据