期刊
ARCHIVES OF CIVIL AND MECHANICAL ENGINEERING
卷 19, 期 2, 页码 557-568出版社
ELSEVIER URBAN & PARTNER SP Z O O
DOI: 10.1016/j.acme.2018.12.010
关键词
Magnetorheological elastomer; Pre-structuring process; Dynamic properties; Taguchi method
资金
- Universiti Sains Malaysia
- School of Materials and Mineral Resources Engineering
- Ministry of Education Malaysia through the FRGS [203/PBAHAN/6071349]
Pre-structuring of magnetic particles during fabrication of magnetorheological elastomer (MRE) is a crucial step, which results in the formation of chain-like columnar structures in the rubber matrix. In this study, MRE based on natural rubber and carbonyl iron particles were prepared. The Taguchi method was utilized to study the effect of several dominating factors during the fabrication process such as pre-curing time, pre-curing temperature and applied magnetic field during curing on the loss tangent (tan delta) and tensile properties. Tan delta was measured through parallel-plate rheometer over a frequency range of 1-100 Hz and a strain amplitude range of 0.1-6%. Tensile properties were measured with a universal tensile testing machine. The obtained data were statistically analyzed using S/N ratios and ANOVA in order to predict the optimal combination of factors, and then further experiments were conducted for verification purpose. Results indicated that the magnetic field had the greatest influence on tan delta when measured over a range of frequency and elongation at break. Furthermore, pre-curing time and magnetic field were found to influence tan delta when measured over a range of strain amplitude. However, none of the factors exhibited significant influence on tensile strength. In addition, the morphology of MRE was examined using scanning electron microscopy (SEM). (C) 2018 Politechnika Wroclawska. Published by Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据