期刊
JOURNAL OF MANUFACTURING PROCESSES
卷 37, 期 -, 页码 362-369出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.jmapro.2018.11.017
关键词
Additive manufacturing; AlSi12; Micro components; Material microstructure; Directed energy deposition
资金
- European Union
- Regione Lombardia
- FESR
- Repubblica Italiana
In this work, micro laser metal wire deposition (mu LMWD) of 0.4 mm diameter 4047 Al-alloy (AlSi12) wire is demonstrated. A flash-pumped Nd:YAG laser producing ms-long pulses was used as the energy source. The processing conditions were studied for single and multi-layered tracks, seeking stable deposition conditions. Microhardness, microstructure and chemical composition were analysed. The results showed that thin walls with sub-mm thickness free of pores and cracks could be obtained using the mu LMWD process. The material was characterized by a homogenous microhardness profile over the build direction with high values (approximately 120 HV). The improved mechanical properties were due to the redistribution of the Si in form of a micrometric network in the Al-matrix along the deposit. The process was found to be a promising option for producing freestanding components, as well as adding features to existing parts with tailored properties, especially for lightweight applications.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据