Enhanced dielectric properties of BaTiO3 ceramics with cerium doping, manganese doping and Ce-Mn co-doping

Ba1-xCexTi1-yMnyO3 (where x and y varies from 0.00 to 0.03) ceramic samples are synthesized by conventional solid state reaction technique. The samples are sintered at 1473 K for 4 h. The grain size is observed to increase with increasing dopant and co-dopant concentration. The X-ray diffraction confirmed the cubic phase of these BaTiO3-based ceramics with a small amount of secondary phase. The current density shows a nearly linear relationship with voltage, and the AC resistivity of the samples is observed to decrease with increasing frequency and doping concentration. The dielectric constant and dielectric loss were observed to decrease with frequency in the lower frequency range (0.2-10 kHz), but remained almost the same at the high-frequency region (>10 kHz). Though Ce-doped samples shows better dielectric properties than Mn-doped samples, the Ce-Mn co-doped samples, having improved their dielectric properties, can be used to fabricate different optoelectric devices.