JOURNAL OF CO2 UTILIZATION
卷 29, 期 -, 页码 57-64出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.jcou.2018.11.006
关键词
Cu-ZnO-ZrO2; LDH; Co-precipitation; CO2 hydrogenation; Methanol
资金
- China Scholarship Council [201606080053]
- University of Melbourne
- Natural Science Foundation of China [51474067]
Methanol synthesis via CO2 hydrogenation is an important part of the strategy for generating clean energy as we attempt to reduce our dependency on fossil fuels. Conventional catalysts for this reaction need improvement in their methanol selectivity. In this work, a layered double hydroxide (Mg-Al LDH) was used as a carrier for Cu-ZnO-ZrO2 to produce a catalyst by co-precipitation. From characterization results, CuO-ZnO-ZrO2 nanoparticles were formed and were uniformly dispersed and attached to the surface of LDH. BET surface area and copper dispersion of the catalysts were significantly improved by 4.3 times and 2.9 times, respectively, compared with a reference catalyst without the support. In a catalytic reaction, the catalyst showed dramatic methanol selectivity of 78.3% at 523 K and 3.0 MPa, which is 14.4% higher than the commercial catalyst measured in this investigation and about 50% higher than conventional copper-based catalysts in literatures. It also showed over twice the space time yield based on active metal sites compared to a commercial catalyst in the temperature range 473 K-573 K. Therefore, the prepared catalyst can be efficiently applied at relatively mild reaction temperatures and pressures.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据