Membrane distillation (MD) purifies water by transporting its vapor through a hydrophobic membrane. An ideal MD membrane poses high water flux and high fouling, scaling, and wetting resistances. In this study, we develop polyvinylidene fluoride (PVDF) membranes for MD by focusing on reduction of PVDF degree of crystallinity. We explore the roles of dope solution temperature in dictating the phase separation mechanisms as well as the structure and the performance of semicrystalline PVDF membranes. DSC spectra show that higher dope solution temperature depresses crystallinity via formation of imperfect crystal. Such findings were also supported by FTIR and XRD results. The SEM images reveal formation of spherulite-like morphology in the membrane matrices for membranes prepared from high temperature dope solutions. A good balance between solid-liquid and liquid-liquid phase separations that offers low degree of crystallinity was found at a dope solution temperature of 60 degrees C (PVDF-60), which showed the MD flux of 18l/m(2) h (vs. 6l/m(2) h for temperature of 25 degrees C, as a benchmark) and nearly complete salt rejection when run at hot and cold temperatures of 65 degrees C and 25 degrees C, respectively. The PVDF-60 shows a high wetting resistance and stable MD flux of 10.5l/m(2) h over a 50h test for treating brine solution as the feed (70g NaCl/l).
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据