DOI: 10.3390/ma11112170
关键词
densification; capillary pressure; cross-linking reaction; specific strength
类别
资金
- Korea Institute of Science and Technology Open Research Program [2E27820]
To increase the strength of carbon nanotube (CNT) fibers (CNTFs), the mean size of voids between bundles of CNTs was reduced by wet-pressing, and the CNTs were cross-linked. Separate and simultaneous physical (roller pressing) and chemical methods (cross-linking) were tested to confirm each method's effects on the CNTF strength. By reducing the fraction of pores, roller pressing decreased the cross-sectional area from 160 mu m(2) to 66 mu m(2) and increased the average load-at-break from 2.83 +/- 0.25 cN to 4.41 +/- 0.16 cN. Simultaneous injection of crosslinker and roller pressing augmented the cross-linking effect by increasing the infiltration of the crosslinker solution into the CNTF, so the specific strength increased from 0.40 +/- 0.05 N/tex to 0.67 +/- 0.04 N/tex. To increase the strength by cross-linking, it was necessary that the size of the pores inside the CNTF were reduced, and the infiltration of the solution was increased. These results suggest that combined physical and chemical treatment is effective to increase the strength of CNTFs.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据