A Comparative Study of Nickel, Cobalt, and Iron Oxyhydroxide Anodes for the Electrochemical Oxidation of 5-Hydroxymethylfurfural to 2,5-Furandicarboxylic Acid

2,5-Furandicarboxylic acid (FDCA) has received increasing attention as a near-market platform chemical that can potentially replace terephthalic acid in the production of commercial and high-performance polymers, such as polyethylene terephthalate. FDCA can be obtained from the oxidation of 5-hydroxymethylfurfural (HMF), which is produced from the dehydration of C-6 monosaccharides obtained from cellulosic biomass. Recently, various heterogeneous Ni- and Co-based electrocatalysts were reported that can efficiently oxidize HMF to FDCA. The actual catalytically active species of these catalysts are most likely NiOOH and CoOOH or species related to NiOOH and CoOOH. However, the intrinsic catalytic properties of NiOOH and CoOOH for HMF oxidation have yet to be carefully and systematically investigated. In this study, we prepared thin and thick sets of NiOOH, CoOOH, and FeOOH films having comparable numbers of metal sites to systematically and methodically compare the intrinsic catalytic activity of these materials for HMF oxidation in a 0.1 M KOH (pH 13) solution. Our investigation revealed that they have distinctively different catalytic abilities for HMF oxidation. The use of extremely thin MOOH films containing limited numbers of catalytic sites allowed us to resolve anodic currents that were generated from HMF oxidation by different oxidation pathways. By comparing the voltammetric results of thin and thick films, the effect of the film thickness on the current generated by different oxidation pathways could be observed. The thick set of MOOH films was also used to compare the performances of these films for constant potential HMF oxidation and product analysis. The work herein contributes to a better understanding of the mechanisms of HMF oxidation on Ni-, Co-, and Fe containing heterogeneous electrocatalysts whose surfaces are covered by their hydroxide and oxyhydroxide phases.