期刊
SURFACE ENGINEERING
卷 35, 期 10, 页码 906-912出版社
TAYLOR & FRANCIS LTD
DOI: 10.1080/02670844.2018.1548101
关键词
Magnesium alloy; zinc dipping; electroless nickel; coating; influence
资金
- Liaoning Provincial Natural Science Foundation [201602648]
- Liaoning Innovation Talents in University [LR2017079]
In this paper, the effect of zinc dipping pretreatment on corrosion resistance of electroless nickel plating on magnesium alloy was studied. The results showed that the corrosion resistance of nickel coating was influenced greatly by the complexing agent and main salt in the zinc dipping solution, and the formula and technological conditions of zinc dipping were optimized by the orthogonal test. The optimum formulation and process conditions were as follows: C4H6O5 40 g L-1, ZnSO4 center dot 7H(2)O 40 g L-1, NaF 4 g L-1, pH 9, temperature 90 degrees C, time 10 min. The corrosion resistance, morphology and phase composition of the nickel coating prepared under the optimum conditions were analysed by SEM, XRD and electrochemical workstation. The results showed that the self-corrosion potential of the nickel coating is 0.87 V higher than the magnesium alloy substrate, the self-corrosion current reduces by two orders of magnitude and the magnesium alloy substrate is completely covered. The corrosion resistance of magnesium alloy was effectively enhanced.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据