期刊
SURFACE & COATINGS TECHNOLOGY
卷 371, 期 -, 页码 262-275出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.surfcoat.2018.11.055
关键词
Thermal barrier coating (TBC); High velocity oxygen fuel (HVOF); Oxidation; Thermal cyclic; YSZ; Gd2Zr2O7 (GZ)
资金
- Scientific and Technological Research Council of Turkey (TUBITAK) [113R049]
- Scientific Research Projects (BAP) Coordinator ship of Karabuk University [KBUBAP-17-DR-202]
Thermal barrier coatings (TBCs) are widely used to increase gas turbine efficiency and to prolong the lifetimes of superalloy substrates. Yttria (7-8%) stabilized zirconia (YSZ) is used as a state of the art TBC top coating material. In recent years, rare earth zirconates have drawn interest as top coating materials due to their high phase transformation temperature and low thermal conductivity. In the present research, CoNiCrAlY powders were sprayed on Inconel 718 superalloy substrates using high velocity oxy fuel (HVOF) deposition technique. YSZ, Gd2Zr2O7 (GZ) and YSZ/GZ top coats were then deposited on the resulting bond coat using EB-PVD technique. The produced TBCs were exposed to isothermal oxidation at 1100 degrees C for 4 different periods, and furnace thermal cyclic tests were conducted at 1150 degrees C. After thermal loadings, TGO (thermally grown oxide) growth behavior and crack surfaces of TBCs were evaluated. Samples were compared with each other using analysis techniques like scanning electron microscopy (SEM), energy dispersive sprectrum (EDS) elemental mapping and X-ray diffraction (XRD) before and after the oxidation tests. The results showed that double layered TBC system is more durable against high temperature degradations.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据