期刊
SOLID STATE SCIENCES
卷 86, 期 -, 页码 1-5出版社
ELSEVIER
DOI: 10.1016/j.solidstatesciences.2018.09.015
关键词
Defect sites; Hydroxyapatite; Phosphate ion; Photocatalyst; Silver orthophosphate
资金
- Ministry of Research, Technology and Higher Education of the Republic of Indonesia [059/SP2H/LT/DRPM/2018]
- JSPS KAKENHI [JP16H06439]
- Dynamic Alliance for Open Innovation Bridging Human, Environment and Materials
- Cooperative Research Program of Network Joint Research Center for Materials and Devices
The effect of hydroxyapatite on structure, particle size, and band gap energy of silver orthophosphate (Ag3PO4) have been investigated. The hydroxyapatite as a source of phosphate ion was prepared using the coprecipitation of Cal(2) and KH2PO4. To produce the product of Ag3PO4, the as-synthesized hydroxyapatite was suspended in water and quickly added to a silver nitrate solution. The obtained photocatalysts were characterized using XRD, SEM, DRS, and XPS. The high crystallinity of single phase Ag3PO4 was easily produced using the hydroxyapatite. Photocatalytic activities of the product were evaluated using RhB decomposition under blue light irradiation. The hydroxyapatite as a source of phosphate ion dramatically decreases the particle size and increases the absorption in the visible region. This obtained photocatalyst significantly improves the photocatalytic activity. The mechanism of reaction works in the following order: holes > superoxide radical > hydroxyl radical.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据