ACTA MATERIALIA
卷 106, 期 -, 页码 48-58出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.actamat.2015.12.051
关键词
Zirconia; Aging; Cation radius; Oxygen vacancy; Grain boundary; Dopant content
资金
- Research Fund of KU Leuven [0T/10/052, PDM/15/153]
- Fund for Scientific Research Flanders (FWO-Vlaanderen) [G.0431.10N]
The hydrothermal aging stability of 3Y-TZP-xM(2)O(3) (M = La, Nd, Sc) was investigated as a function of 0.02 -5 mol% M2O3 dopant content and correlated to the overall phase content, t-ZrO2 lattice parameters, grain size distribution, grain boundary chemistry and ionic conductivity. The increased aging stability with increasing Sc2O3 content and the optimum content of 0.4-0.6 mol% Nd2O3 or 0.2-0.4 mol% La2O3, resulting in the highest aging resistance, could be directly related to the constituent phases and the lattice parameters of the remaining tetragonal zirconia. At low M2O3 dopant contents <= 0.4 mol%, the different aging behavior of tetragonal zirconia was attributed to the defect structure of the zirconia grain boundary which was influenced by the dopant cation radius. It was observed that the grain boundary ionic resistivity and the aging resistance followed the same trend: La3+ > Nd3+ > Al3+ > Sc3+, proving that hydrothermal aging is driven by the diffusion of water-derived mobile species through the oxygen vacancies. Accordingly, we elucidated the underlying mechanism by which a larger trivalent cation segregating at the zirconia grain boundary resulted in a higher aging resistance. (C) 2016 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据