期刊
ACTA MATERIALIA
卷 102, 期 -, 页码 88-96出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.actamat.2015.08.079
关键词
BiCuSeO; Thermoelectric; Oxidation state; Charge compensation; XPS
资金
- Ministry of Science and Technology, Taiwan [MST-102-2221-E-006-057-MY3]
- National Cheng Kung University via the Top University Projects
Bi1-xCaxCuSeO (x = 0-0.3) was synthesized at 650 degrees C in an air-tight system flowing with pure argon. The Ca doping resulted in an increase in the thermoelectric figure of merit (ZT) as the consequence of increased carrier concentration. X-ray photoelectron spectroscopy (XPS) was carried out to check the oxidation states in Bi1-xCaxCuSeO. The results indicated that in addition to the expected Bi3+ and Cu1+, there existed Bi2+ and Cu2+ in the undoped BiCuSeO, whereas in the Ca-doped BiCuSeO, Bi4+, Cu3+ and Cu2+ were observed. The Ca dopant was confirmed to be in the 2+ oxidation state. Two broad peaks centered at 54.22 and 58.59 eV were recorded in the vicinity around the binding energy of Se 3d. The former is often observed in the Se-containing intermetallics while the latter is often found in the Se-containing oxides, indicating that along with the expected Se-Cu bonding, a bonding between Se and O may also exist. Based on the XPS results, the charge compensation mechanisms were proposed for Bi1-xCaxCuSeO, which may shed some light on the origins of charge carriers. BiCuSeO based oxides have recently be discovered to have a large ZT comparable to the best alloys currently in use, because of the large Seebeck coefficient and small thermal conductivity. However, their electrical conductivity is lower compared to the best thermoelectrics. This work may provide some hints for the further improvement of Zr in BiCuSeO based oxides. (C) 2015 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据