In this study, it was aimed to increase the piezoelectric and pyroelectric properties of electrospun polyvinylidene fluoride (PVDF) nanofibers simultaneously by using specific nanofillers. Graphene oxide (GO), graphene, and halloysite nanotubes with different concentrations (0, 0.05, 0.4, and 1.6% wt/wt) were combined with PVDF solution and were fabricated in the form of nanofibers through electrospinning. Pyroelectric properties of samples were measured by submerging sealed samples in hot water (360 degrees K) and ice (270 degrees K). The piezoelectric properties of the samples were evaluated through bending tests. The microstructural, mechanical, and thermal properties of the electrospun PVDF nanocomposite were investigated using scanning electron microscope, Instron instrument, and thermogravimetric analysis, respectively. To further support the experimental observations for generating electric voltage in the bended nanogenerator, the PVDF nanogenerator (PNG) was also modeled by a finite element analysis based on the theory of linear piezoelectricity using COMSOL Multiphysics simulation software. Experimental results showed that adding nanofillers could improve the piezoelectric and pyroelectric properties of all samples, associated with the increment of beta-phase in the nanofibers. It was concluded that adding nanofillers could increase pyroelectricity about 50% more than piezoelectricity in pristine PVDF nanofiber web. The PNG containing 1.6 wt% GO showed the highest efficiency in terms of piezoelectricity and pyroelectricity. In addition, the results showed that the ratio of piezoelectric to pyroelectric coefficients was constant (similar to 1.5) and it was independent of the nanofiller type and content. The effect of external force and vibration frequency on the output voltage was also investigated. Increasing the compressive force and vibration frequency caused a greater output voltage. Finally, the fabricated nanogenerator was integrated on insole and elbow to investigate its energy harvesting capabilities from body movement.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据