ACS APPLIED MATERIALS & INTERFACES
卷 8, 期 28, 页码 18505-18512出版社
AMER CHEMICAL SOC
DOI: 10.1021/acsami.6b06189
关键词
proton conductivity; covalent organic frameworks; mechanoassisted synthesis; mixed matrix membranes; proton exchange membranes
资金
- National University of Singapore (CENGas) [R-261-508-001-646]
- Singapore Ministry of Education (MOE AcRF) [R-279-000-410-112]
- National Natural Science Foundation of China [21233006, 21473164, 21403202]
It is challenging to introduce pendent sulfonic acid groups into modularly built crystalline porous frameworks for intrinsic proton conduction. Herein, we report the mechanoassisted synthesis of two sulfonated covalent organic frameworks (COFs) possessing onedimensional nanoporous channels decorated with pendent sulfonic acid groups. These COFs exhibit high intrinsic proton conductivity as high as 3.96 X 10(-2) S cm(-1) with long-term stability at ambient temperature and 97% relative humidity (RH). In addition, they were blended with nonconductive polyvinylidene fluoride (PVDF) affording a series of mixed-matrix membranes (MMMs) with proton conductivity up to 1.58 x 10(-2) S cm(-1) and low activation energy of 0.21 eV suggesting the Grotthuss mechanism for proton conduction. Our study has demonstrated the high intrinsic proton conductivity of COFs shedding lights on their wide applications in proton exchange membranes.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据