期刊
ACS APPLIED MATERIALS & INTERFACES
卷 8, 期 11, 页码 7422-7430出版社
AMER CHEMICAL SOC
DOI: 10.1021/acsami.5b12072
关键词
phthalonitrile; carbonization; carbon foam; compressive strength; EMI shielding
资金
- Nanyang Technological University (NTU) [M4061124]
- School of Materials Science and Engineering and Electromagnetic Effect Research Laboratory at NTU
Electromagnetic interference (EMI) performance materials are urgently needed to relieve the increasing stress over electromagnetic pollution problems arising from the growing demand for electronic and electrical devices. In this work, a novel ultralight (0.15 g/cm(3)) carbon foam was prepared by direct carbonization of phthalonitrile (PN)-based polymer foam aiming to simultaneously achieve high EMI shielding effectiveness (SE) and deliver effective weight reduction without detrimental reduction of the mechanical properties. The carbon foam prepared by this method had specific compressive strength of similar to 6.0 MPa-cm(3)/g. High EMI SE of similar to 51.2 dB was achieved, contributed by its intrinsic nitrogen-containing structure (3.3 wt% of nitrogen atoms). The primary EMI shielding mechanism of such carbon foam was determined to be absorption. Moreover, the carbon foams showed excellent specific. EMI SE of 341.1 dB.cm(3)/g, which was at least 2 times higher than most of the reported material. The remarkable EMI shielding performance combined with high specific compressive strength indicated that the carbon foam could be considered as a low-density and high-performance EMI shielding material for use in areas where mechanical integrity is desired.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据