Austenitic boiler tubes; Shot-peening; Steam oxidation; Scale; TEM
类别
资金
- Korea Institute of Energy Technology Evaluation and Planning (KETEP)
- Ministry of Trade, Industry & Energy (MOTIE) of the Republic of Korea [20161110100090]
Steam oxidation of a Super 304H boiler tube was performed at steam temperatures of 650 degrees C and 700 degrees C for time durations up to 5000 h. The oxidation scale outcomes which formed on as-received untreated and shot-peened (SP) tubes were studied using X-ray diffraction (XRD), scanning electron microscopy (SEM), electron backscatter diffraction (EBSD), and transmission electron microscopy (TEM). gamma-Grain nanocrystallization on the surface of the SP specimen generated an abundant fraction of grain boundary that guaranteed the formation of a continuous amorphous SiO2 layer at the metal-scale interface that enhanced the formation of dense Cr2O3 and FeCr2O4 in the scale. Scale breakaway along defects in the outer layer of the scale was accelerated by the steam temperature in the untreated specimens, whereas the scale that formed on the SP specimens appeared to be stable.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据