sodium ion batteries; cathode; Na3V2(PO4)(3)/C; nickel substitution; Na-rich
资金
- National Basic Research Program of China [2015CB251100]
- Program for New Century Excellent Talents in University [NCET-13-0033]
- Beijing Co-construction Project [20150939014]
In order to get an, element substituted into Na3V2(PO4)(3)/C in an appointed V site, the simple sol gel method is used to design and prepare a series of Na-rich Na3+xV2- Ni-x(x)(PO4)(3)/C (x = 0-0.07) compounds. To get a charge balance, the ratio of Na, V, and Ni would be changed if Ni goes into a different site. Hence, ICP is applied to probe the real stoichiometry of the as-prepared Na3+xV2- Ni-x(x)(PO4)(3)/C (x = 0-0.07). According to the Na/V ratio from the ICP result, it indicates that Ni2+ goes to a V site, and more Na+ will be introduced into the crystal to keep the charge balance. In addition, the crystal structure changes are explored by XRD and Rietveld refinement, it is indicated from the results that Ni2+ doping does not destroy the lattice structure of Na3V2(PO4)(3). When applied as Na-storage material, the electrochemical property of all Ni2+ doped Na3+xV2- Ni-x(x)(PO4)(3)/C composites have been significantly improved, especially for the Na3.03V1.97Ni0.03(PO4)(3)/C sample. For example, 107.1 mAh g(-1) can be obtained at the first cycle; after 100 cycles, the capacity retention is as high as 95.5%. Moreover, when charging/discharging at a higher rate of 5 C, the capacity still remains 88.9 mAh g(-1), displaying good rate performance. The good electrochemical performance is ascribed to the optimized morphology, stable crystal structure, and unproved ionic conductivity.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据