期刊
JOURNAL OF NON-CRYSTALLINE SOLIDS
卷 503, 期 -, 页码 224-231出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.jnoncrysol.2018.09.048
关键词
Glass formation; Thermal stability; Structure
In this study we determined the glass formation region in the TeO2 - ZnO - Bi2O3 - Nb2O5 system. The investigation covers TeO2 - based glasses containing ZnO (from 10 to 40 mol%), Bi2O3 (6-10 mol%) and Nb2O5 (6-10 mol%). The glasses obtained were transparent and yellow in colour. The thermal stability of the samples determined by DTA was found to be about 100 degrees C. Some physical characteristics (density, molar volume, oxygen molar volume and oxygen packing density) were estimated as well. The analysis of IR spectra showed that the network of glasses consists mainly of TeO4 (tbp) units, while Raman spectroscopy revealed the existence of TeO4 (tbp), TeO3+1 and TeO3 (tp) units. The UV-Vis spectroscopy established a red shifting of the cut-off depending on composition and the glass rich in TeO2 exhibited cut-off at about 388 nm while that with low TeO2 content was 378 nm.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据