JOURNAL OF MATERIALS SCIENCE-MATERIALS IN ELECTRONICS
卷 30, 期 5, 页码 4409-4426出版社
SPRINGER
DOI: 10.1007/s10854-019-00730-5
关键词
XRD; Charge density; Ferromagnetism; Dielectric constant; AC conductivity
Strontium (Sr) substituted LaFeO3 (La1-xSrxFeO3) (x=0.05, 0.10, 0.15 and 0.20) multiferroics were synthesized by the conventional high temperature solid-state reaction method. The X-ray diffraction was used to analyze the phase formation and purity of La1-xSrxFeO3 multiferroics. The X-ray diffraction patterns confirm that all the samples are monophasic with orthorhombic structure. The charge density distribution and the interatomic chemical bonding between the neighbouring atoms in the unit cell were examined using the structure factors obtained through the refinement process. SEM micrographs were used to observe the surface morphology and to determine the average particle size. UV-Vis spectrographs and magnetic hysteresis (M-H) loops from magnetic measurements were exploited to investigate the optical and magnetic behavior of the samples. The magnetic hysteresis loops indicate that the prepared La1-xSrxFeO3 multiferroics exhibit ferromagnetic behavior. Ferromagnetism was observed to be relatively prominent for x=0.05 sample, with high values of magnetic parameters such as M-s, M-r, and H-C as 2.4emu/g, 1.12emu/g, and 1616 G respectively. The dielectric measurements indicate that the sample with Sr content x=0.05, attains the giant value of dielectric constant of about 2.3x10(5) and ac conductivity of about 0.2(-1)m(-1) when compared to the other samples. The optical, magnetic and dielectric properties of La1-xSrxFeO3 multiferroics have been examined and also have been correlated with the charge, bonding nature and the spin of the constituent ions which has not been explored in open literature so far.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据