JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY
卷 35, 期 1, 页码 94-99出版社
JOURNAL MATER SCI TECHNOL
DOI: 10.1016/j.jmst.2018.09.022
关键词
Friction stir welding; Ultrasonic; Aluminum/titanium alloys; Microstructure; Mechanical properties
Ultrasonic assisted friction stir welding (UaFSW) was used to join 6061-T6 aluminum and Ti6Al4V alloys. A small plunge depth endowed with the low heat input was used and the sound joints without obvious thickness reduction were achieved. A diffusion-type bonding without the intermetallic compounds layer was observed at the joint interface. The ultrasonic improved the diffusion thickness and decreased the average size of grains and titanium alloy fragments. A hook-like structure was formed at the bottom interface of the UaFSW joint, which improved the bonding length and the mechanical interlocking. The microhardness of the stir zone was increased because of the further grain refinement induced by ultrasonic. The maximum tensile strength of the UaFSW joint was 236 MPa, which reached 85% of the base 6061-T6 alloy. (C) 2018 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据