期刊
JOURNAL OF ALLOYS AND COMPOUNDS
卷 770, 期 -, 页码 267-275出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.jallcom.2018.08.107
关键词
Graphite flake; Composites; Interfacial layer; Thermal conductivity
资金
- National Key R&D Program of China [2016YFB0301400]
- National Natural Science Foundation of China [51274040]
Graphite flake/Cu composites with Zr element introduced into the matrix were successfully fabricated by vacuum hot pressing. The influence of Zr addition on the phase composition, microstructure and properties were investigated. The results indicate that the bending strength in X-Y plane gradually rises with the Zr content increasing from 0 to 2.0 wt%, nearly doubled from 50 MPa to 95 MPa. The thermal conductivity in X-Y plane initially increases and then decreases, yielding a maximum of 640 W m(-1) K-1 at 1.0 wt% Zr. This improvement is ascribed to the formation of carbide interfacial layer at the graphite flake/Cu interface. Due to the simple preparation process and excellent thermal conductivity, the graphite flake/Cu composites with moderate Zr addition can be a highly promising candidate for thermal management materials. (C) 2018 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据