Pulsed laser deposition and characteristics of epitaxial non-polar m-plane ZnO1-xSx alloy films

Non-polar m-plane ZnO1-xSx (ZnOS) thin films were grown epitaxially on m-plane sapphire using pulsed laser deposition for the first time. Effects of the growth temperature on the surface morphology, as well as on the structural and optical properties of the films were investigated. The S content in the ZnO1-xSx alloy films was adjusted by controlling the substrate temperature. X-ray diffraction analyses revealed that, the ternary ZnO1-xSx films changed from polycrystalline to monocrystalline-like with increasing growth temperature, and m-plane orientated ZnO1-xSx thin films were achieved at temperatures above 400 degrees C. The films with S content below 28 at% exhibit a unique non-polar (10 (1) over bar0) orientation. For the films grown at 300 degrees C with S content above 34 at%, however, additional diffraction peaks from (0002) and (11 (2) over bar0) planes are present. The phi-scan patterns suggest the following in-plane epitaxial relationship: ZnOS(0001) parallel to sapphire(1 (2) over bar 10) and ZnOS(1 (2) over bar 10) parallel to sapphire(0001). With the S content increasing from 12 at% to 28 at%, the lattice constant a of m-plane ZnO1-xSx films expands monotonically from 3.299 to 3.698 angstrom, while their optical bandgaps decrease from 3.05 to 2.95 eV. Differing from the c-plane ZnOS films, the m-plane ZnOS films exhibit anisotropic crystalline quality, extended S solubility, and nearly non-bowing bandgap tunability with the S content. This first-hand information is useful for future rational design of m-ZnOS-based junctions and optoelectronic devices. (C) 2018 Elsevier B.V. All rights reserved.