INDUSTRIAL LUBRICATION AND TRIBOLOGY
卷 71, 期 3, 页码 459-466出版社
EMERALD GROUP PUBLISHING LTD
DOI: 10.1108/ILT-03-2018-0092
关键词
Oxidation; Porous polyimide; Solid; liquid lubricating; WS2 film
资金
- National Natural Science Foundation of China [51505463]
- National Natural Science Foundation of China Aerospace Science and Technology Corporation of China Aerospace Advanced Manufacturing Technology Research Joint Fund [U1637205]
Purpose This paper aims to study the tribological behavior of the WS2/oil-impregnated porous polyimide (PPI) solid/liquid composite system, in which both PFPE (perfluoropolyether) and SiCH (silahydrocarbons) oils with different hydrocarbon chains were used, respectively. Lubricating mechanism of the composite system was also explored. Design/methodology/approach The tribological behaviors of the WS2 films against the PPI cylindrical pins before and after immersing oil were evaluated under different loads by a reciprocating-type ball-on-disc tribometer. Findings The composite system exhibited the low and stable friction coefficient after the running-in stage, and the lubricant oil played a positive effect. It was found that the WS2/PFPE composite system exhibited more excellent lubricating property, although sole SiCH far exceeds PFPE in lubrication. The abnormal phenomenon mainly resulted from the influence of the oil amount. XRD results on the wear track surfaces indicated that PFPE and SiCH oils with different hydrocarbon chains were likely to preferentially adsorb to the edge plane and basal plane of the WS2 crystals, respectively. Originality/value In previous studies, liquid lubricants were directly dripped or spin-coated on the solid lubricant surface. Based on its potential advantage in application, the tribological behavior and mechanism of the solid lubricating film/oil-impregnated PPI composite system were investigated in this study.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据