期刊
INDUSTRIAL & ENGINEERING CHEMISTRY RESEARCH
卷 58, 期 4, 页码 1561-1569出版社
AMER CHEMICAL SOC
DOI: 10.1021/acs.iecr.8b02904
关键词
-
资金
- Marie Curie grant from the European Commission in the framework of the MINSC ITN (Initial Training Research network) [290040]
- German Helmholtz Recruiting Initiative
The effects that 20 ppm poly(epoxysuccinic acid) (PESA), poly(aspartic acid) (PASP), and two poly(acrylic acid) (PAA) compounds with molecular weights of similar to 2000 and similar to 100 000 have on the crystallization of gypsum were evaluated at 21 degrees C by in situ UV-vis spectrophotometry. XRD and SEM were utilized for phase and morphological studies, while the way these additives are associated with the final gypsum crystals was evaluated by XPS. The comparison showed that PASP performed far better than the other antiscalants as it completely inhibited the formation of gypsum. In contrary, the presence of the low molecular weight PAA decreased the rate of crystallization far more than the larger molecular weight PAA. When the pH in the reacting solution was switched from similar to 4 to similar to 7, the efficiency of the low molecular weight PAA in inhibiting gypsum formation increased, while in the presence of the higher molecular weight PAA the opposite effect was observed.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据