FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES
卷 42, 期 3, 页码 597-611出版社
WILEY
DOI: 10.1111/ffe.12935
关键词
fatigue crack propagation; plastically mismatched interface; plasticity induced crack closure
资金
- National Natural Science Foundation of China [11672151, U1533134, 11632010, 11572171, 11372151]
- Science and Technology Fund of Beijing Education Committee [KM201710853003]
- State Key Laboratory of Explosion Science and Technology (Beijing Institute of Technology) [KFJJ15-12M, KFJJ11-9Y]
In the present work, comprehensive investigation of both theoretical analysis and numerical simulation was carried out to investigate the plastic mismatch effect on plasticity induced crack closure (PICC) behavior and effective fatigue crack tip driving force. During the process of crack tip approaching interface, crack tip load and crack tip load ratio will change, resulting in the change of PICC degree. When the crack propagates towards higher strength side, K-op/K-max increases; when the crack propagates towards lower strength side, K-op/K-max decreases firstly and then increases. The two mechanisms of interface plastic mismatch effect on nominal fatigue crack tip driving force and interface plastic mismatch effect on PICC degree were compared. The second mechanism must be considered when building crack tip driving force model for describing fatigue crack crossing plastically mismatched interface, because it is more physically factual and maybe more important than the first mechanism.