Synthesis of coal fly ash zeolite for the catalytic wet peroxide oxidation of Orange II

期刊

ENVIRONMENTAL SCIENCE AND POLLUTION RESEARCH
卷 26, 期 5, 页码 4277-4287

出版社

SPRINGER HEIDELBERG
DOI: 10.1007/s11356-018-3315-1

关键词

Fly ash; Zeolite; Geo-catalyst; Fenton reaction; Orange II; Mineralization; Discoloration

资金

  1. CONICET (Argentina)
  2. AUIP (Spain)

向作者/读者索取更多资源

Fly ash, a coal combustion residue produced by Termotasajero in Colombia, has been hydrothermally treated after an alkaline fusion to produce zeolite without addition of silicon or aluminum. The starting material was thoroughly mixed with NaOH, in a 1:1.2 mass ratio, to obtain a homogeneous mixture that was heated to 100 A degrees C during different times (6, 8, and 10 h) and three zeolite samples were produced. The samples were characterized by XRD, SEM, XRF, Mossbauer spectroscopy, and N-2 physisorption. According to characterization results (high surface area and appropriate morphological properties including crystallinity) and synthesis time, zeolitic catalyst synthesized with 8 h of hydrothermal treatment was selected to perform further analysis. This sample consisted of a mixture of zeolite X and zeolite A of high surface area (301 m(2) g(-1)) and a Fe content of 6% wt/wt. The zeolite was used as a catalyst for the Fenton oxidation of Orange II. Experiments were performed in a laboratory batch reactor at 70 A degrees C and constant pH = 3, using different concentrations of H2O2. When the stoichiometric amount of H2O2 was used, good mineralization (X (TOC) = 45%), complete discoloration, and oxidant consumption were obtained after 240 min of reaction. The sample retained activity after 16 h of usage. The presence of Fe in the reaction media was always detected and a homogeneous Fenton mechanism induced by surface-leached iron is suggested.

作者

我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。

评论

主要评分

4.7
评分不足

次要评分

新颖性
-
重要性
-
科学严谨性
-
评价这篇论文

推荐

暂无数据
暂无数据