ENGINEERING FAILURE ANALYSIS
卷 95, 期 -, 页码 18-29出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.engfailanal.2018.08.029
关键词
PWHT; PWNT; Creep; Microstructure; Fracture surface
In the present research work, P91 steel plates of thickness 18 mm were welded using the shielded metal arc welding process. The welded steel plate subjected to different heat treatment condition including post weld heat treatment (760 degrees C for 2 h, followed by air cooling) and re-austenitizing (1040 degrees C for 60 min and air cooled) and tempered (760 degrees C for 2 h, followed by air cooling). The heat treatments were referred as the PWHT and PWNT. The creep sample was prepared to form the welded and heat treated plate. The creep tests were performed at 620 degrees C for stresses of 150 and 200 MPa. The weld fusion zone and fine-grained heat affected zone of the crept sample were characterized using the field emission scanning electron microscope (FESEM). The fracture surface morphology of crept sample was also studied using the FESEM. The maximum creep exposure time was measured for the PWNT sample as a result of homogeneous microstructure across the weldments.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据