CERAMICS INTERNATIONAL
卷 45, 期 6, 页码 7696-7702出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.ceramint.2019.01.070
关键词
Transparent ceramics; Optical thermometry; Upconversion luminescence; Rare earth
资金
- Natural Science Foundation of Zhejiang Province [LY18E020008, LZ14B010001]
Ho3+ /Yb3+ codoped (Y0.88La0.09Zr0.03)(2)O-3 transparent ceramics were prepared by a high temperature solid-state reaction method. SEM observation confirms that there are no obvious impurities or pores existed in the grain boundaries of the samples. Accordingly, all the samples show excellent transparency in the visible and near-infrared range. Upon 980 nm excitation, strong green emission peaked at 549 nm, red emissions centered at 667 and 756 nm, as well as near infrared emission located at 2 pm respectively from Ho3+ ions are observed. By utilizing the fluorescence intensity ratio (FIR) technique, the temperature sensing behaviors of the optimal sample (Yb0.03Ho0.01Y0.84La0.09Zr0.03)(2)O-3 are investigated at different excitation power densities based on the non-thermally coupled levels of F-5(4)/S-5(2) and F-5(5). The thermometry is found to be immune to the excitation power density, leading to the consistent calibration curves and sensing sensitivities at the different power densities. The maximal sensing sensitivity is about 71.28 x 10(-4) K-1 at 563 K. The results indicate that the Ho3+ /Yb3+ codoped (Y0.88La0.09Zr0.03)(2)O-3 transparent ceramics are promising for the temperature sensors, display devices and 2 mu m solid-state lasers.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据