卷 2, 期 1, 页码 65-73出版社
WILEY
DOI: 10.1002/fsn3.81
关键词
Antibacterial properties; gelatin; mechanical properties; MWCNT; water resistance
资金
- Shiraz University [88-GR-AGRST-108]
Gelatin composite films were prepared from gelatin solutions (10% w/v) containing multi-walled carbon nanotubes (MWCNT, 0.5, 1, 1.5, and 2% w/w gelatin) as nanofiller. The water solubility, water swelling, water uptake, water vapor permeability (WVP), mechanical, and antibacterial properties of the films were examined. Water solubility, water swelling, water uptake, and WVP for gelatin films were 45 +/- 1%, 821 +/- 42%, 45 +/- 1.1%, and 0.4 +/- 0.022 g mm/m(2) kPa h, respectively. Incorporation of MWCNT caused a significant decrease in water solubility, water swelling, water uptake, and WVP. Gelatin/MWCNT films containing 1-1.5% MWCNT showed the lowest water vapor transmission. Tensile strength, elongation at break, and Young's modulus for gelatin films were 13.4 +/- 1.2 MPa, 95 +/- 5%, and 45.4 +/- 7 MPa, respectively. Incorporation of MWCNT caused a significant increase in tensile strength and decrease in the elongation at break. The largest mechanical strength was found at 1.5% MWCNT. All gelatin/MWCNT films showed significant antibacterial activities against both gram-positive and gram-negative bacteria. Our results suggest that the gelatin/MWCNT composites films could be used as a very attractive alternative to traditional materials for different biomedical and food applications.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据