期刊
JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T
卷 4, 期 4, 页码 416-422出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.jmrt.2015.02.004
关键词
ZrB2-SiC composites; Pressureless sintering; Microstructure; Mechanical properties
In the present paper, ZrB2-SiC composites were prepared by pressureless sintering at temperatures of 2000-2200 degrees C for 1 h under argon atmosphere. In order to prepare composite samples, ZrB2 powder was milled for 2 h, then the reinforcing particles including of micron and nano-sized SiC powder were added. The mixtures were formed and, after the pyrolysis, they were sintered. Densification, microstructural and mechanical properties of ZrB2-SiC composites were investigated. The shrinkage of samples was measured both before and after the sintering, and the microstructure of samples was examined using scanning electron microscopy (SEM), equipped with EDS spectroscopy. Both mass fraction and size of SiC powder have a great effect on relative density, porosity, shrinkage, hardness and microstructure of these composites. The highest relative density and hardness were 98.12% and 15.02 GPa, respectively, in ZrB2-10 wt% SiCnano composite sintered at 2200 degrees C. (C) 2015 Brazilian Metallurgical, Materials and Mining Association. Published by Elsevier Editora Ltda. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据