Structural and magnetic properties of nanocrystalline BaFe12O19 synthesized by microwave-hydrothermal method

Nanocrystalline BaFe12O19 powders were prepared by microwave-hydrothermal method at 200 degrees C/45 min. The as-synthesized powders were characterized by using X-ray diffraction (XRD), thermogravimetry (TG) and differential thermal analysis (DTA). The present powders were densified at different temperatures, i.e., 750, 850, 900 and 950 degrees C for 1 h using microwave sintering method. The phase formation andmorphology studies were carried out using XRD and field emission scanning electron microscopy (FE-SEM). The average grain sizes of the sintered samples were found to be in the range of 185-490 nm. The magnetic properties such as saturation magnetization and coercive field of sintered samples were calculated based on magnetization curves. A possible relation between the magnetic hysteresis curves and the microstructure of the sintered samples was investigated.