JOURNAL OF MANUFACTURING PROCESSES
卷 35, 期 -, 页码 657-663出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.jmapro.2018.09.014
关键词
Explosive welding (EXW); Heat treatment; Interface; Microhardness; Shear strength; Intermetallic compound (IMC)
In the current research, microstructure evolution and mechanical properties of multilayer Cu/Al/Cu explosive welded joints were studied at upper and lower interfaces after heat treatment. To investigate the effects of time and temperature on joints, welded samples were annealed at 300 and 400 degrees C for different soaking times of 30 min and 20 h. Joints were analyzed by optical microscope (OM), scanning electron microscope (SEM), microhardness and shear strength tests along with interface composition change by means of energy dispersive spectroscopy (EDS). Results revealed that the average thickness of diffusion layer had been increased by enhancement of treatment variables. This was associated with the microhardness of diffusion layer at both interfaces. Meanwhile, tensile-shear strengths of joints were reduced after annealing due to the layer thickness increment of intermetallic compounds (IMCs). Microchemical analyses proved that not only layer thickness experienced alteration, but also, types of IMCs had evolution at interfaces. Doi ng this, evolution of diverse compounds of AlCu, Al2Cu, Al3Cu, and Al3Cu2 were experienced. Obtained results elucidated that the thickness of diffusion layer had direct correlation with both temperature and time of applied thermal cycles.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据