ACS BIOMATERIALS SCIENCE & ENGINEERING
卷 4, 期 9, 页码 3327-3346出版社
AMER CHEMICAL SOC
DOI: 10.1021/acsbiomaterials.8b00624
关键词
conducting polymer; MEH-PPV; surface functionalization; electrical stimulation; neural tissue engineering
资金
- British Council, U.K.
- Department of Biotechnology (DBT), Government of India
- Department of Science & Technology (DST), Government of India, through Inspire Fellowship Scheme
In the present study, a conducting polymer, poly[2-methoxy-5-(2-ethylhexyloxy)-1,4-phenylenevinylene] (MEH-PPV) along with a biodegradable polymer poly(epsilon-caprolactone) (PCL) was used to prepare an electrically conductive, biocompatible, bioactive, and biodegradable nanofibrous scaffold for possible use in neural tissue engineering applications. Core-sheath electrospun nanofibers of PCL as the core and MEH-PPV as the sheath, were surface-functionalized with (3-aminopropyl) triethoxysilane (APTES) and 1,6-hexanediamine to obtain amine-functionalized surface to facilitate cell biomaterial interactions with the aim of replacing the costly biomolecules such as collagen, fibronectin, laminin, and arginyl-glycyl-aspartic acid (RGD) peptide for surface modification. Scanning electron microscopy (SEM) and transmission electron microscopy (TEM) confirmed the formation of core sheath morphology of the electrospun nanofibers, whereas Fourier-transform infrared spectroscopy (FTIR) and X-ray photoelectron spectroscopy (XPS) revealed successful incorporation of amine functionality after surface functionalization. Adhesion, spreading, and proliferation of 3T3 fibroblasts were the surface-functionalized electrospun meshes, whereas the neuronal model rat pheochromocytoma 12 (PC12) adhered and differentiated into sympathetic neurons on these meshes. Under a constant electric field of 500 mV for 2 h/day for 3 consecutive days, the PC12 cells displayed remarkable improvement in the neurite formation and outgrowth on the surface-functionalized meshes that was comparable to those on the collagen-coated meshes under no electrical signal. Electrical stimulation studies further demonstrated that electrically stimulated PC12 cells cultured on collagen I coated meshes yielded more and longer neurites than those of the unstimulated cells on the same scaffolds. The enhanced neurite growth and differentiation suggest the potential use of these scaffolds for neural tissue engineering applications.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据