期刊
MINERALS
卷 8, 期 9, 页码 -出版社
MDPI
DOI: 10.3390/min8090389
关键词
pellet; MgO; induration; unreacted core model; oxide densification index (ODI)
资金
- National Science Foundation of China [51604069, 51774071, 51874080]
- Fundamental Research Funds for the Central Universities, China [N162504004]
The induration process of oxidized pellet, containing the oxidation of magnetite phase (Fe3O4) and the sintering of oxidized magnetite phase (hematite-Fe2O3), is significant to obtain sufficient pellet strength. The current study focuses on the induration mechanisms of MgO flux pellet in terms of the oxidation process of Fe3O4 and densification process of the pellet. It is found that MgO dosage negatively affects the oxidation of Fe3O4 into Fe2O3. The number of recrystallized grain of Fe2O3 in the MgO flux pellet is less than that in the Non-MgO flux pellet. Additionally, an unreacted core model was applied to consider and clarify the oxidation of Fe3O4. According to the verification experiments, the experimental data and calculated results fit well. Therefore, the unreacted core model can describe the oxidation of Fe3O4 in the pellet induration process. Moreover, based on the development of pore parameters during the pellet induration process, a new index, the so-called oxide densification index (ODI) was defined to profoundly specify the densification degree of the pellet. The results show that the ODI of the MgO flux pellet maintains at a lower level compared with that of the Non-MgO flux pellet. It illustrates that MgO can substantially restrain the pellet densification process.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据