supercapacitor; carbon electrode; carbonization temperature
资金
- Carbon Valley Project of the Korea Government (Ministry of Commerce, Industry and Energy)
- Korea Ministry of Environment (MOE)
Nitrogen-doped microporous carbons were prepared using a polyvinylidene fluoride/melamine mixture. The electrochemical performance of the nitrogen-doped microporous carbons after being subjected to different carbonization conditions was investigated. The nitrogen to carbon ratio and specific surface area decreased with an increase in the carbonization temperature. However, the maximum specific capacitance of 208 F/g was obtained at a carbonization temperature of 800 degrees C because it produced the highest microporosity.