JOURNAL OF MATERIALS CHEMISTRY B
卷 2, 期 28, 页码 4426-4434出版社
ROYAL SOC CHEMISTRY
DOI: 10.1039/c4tb00061g
关键词
-
资金
- European project Magnifyco [NMP4-SL-2009-228622]
- Italian AIRC project [14527]
- Italian FIRB projects Nanostructure oxides [588 BAP115AyN]
We report a highly reproducible route to synthesize iron oxide nanoparticles (IONPs) with control over size and shape and with size dispersions around 10%. By tuning the relative ratio of squalane to dibenzyl ether, which were used as solvents in the synthesis, the size of the particles could be varied from 14 to around 100 nm, while their shape evolved from cubic (for size ranges up to 35 nm) to truncated octahedra and octahedra (for sizes from 40 nm up to 100 nm). Fine tuning of the size within each of these ranges could be achieved by varying the heating ramp and the iron precursor to decanoic acid ratio. We also demonstrate direct water transfer of the as-synthesized IONPs via in situ ligand exchange with gallol polyethylene glycol molecules, the latter simply added to the crude nanocrystal mixture at 70 degrees C. The specific absorption rate (SAR) values measured on the water transferred IONPs, at frequencies and applied magnetic fields that are considered safe for patients, confirmed their high heating performance. Finally, this method allows the transfer of 35 nm nanocubes as individually coated and stable particles to the water phase. For the first time, the heating performance of such large IONPs has been studied. This work uncovers the possibility of using large IONPs for magnetic hyperthermia in tumor therapy.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据