期刊
JOURNAL OF MATERIALS CHEMISTRY A
卷 2, 期 40, 页码 16905-16914出版社
ROYAL SOC CHEMISTRY
DOI: 10.1039/c4ta03732d
关键词
-
资金
- National Natural Science Foundation of China [51274106, 11204108]
- China Postdoctoral Science Foundation [2013M510418]
- Science and Technology Support Program of Jiangsu Province [BE2012143, BE2013071]
- Natural Science Foundation of the Jiangsu Higher Education Institutions of China [11KJB430006, 12KJA430001]
- Jiangsu Planned Projects for Postdoctoral Research Funds [1301055B]
Carbon nanofibers with ferromagnetic metal nanopartictes (CNF-M, M = Fe, Co, and Ni) have been synthesized by carbonizing electrospun polyacrylonitrile nanofibers including metal acetytacetonate in an argon atmosphere, and their phase composition, microstructure, magnetic properties and electromagnetic (EM)-wave absorbability have been studied. The microstructure analysis shows that the in situ formed metal nanopartictes are well distributed along carbon-based nanofibers and encapsulated by ordered graphite layers. The investigation of magnetic properties and EM-wave absorbability reveals that the as-synthesized CNF-M has typical characteristics of ferromagnetic materials and exhibits excellent EM-wave absorption properties (reflection loss exceeding -20 dB) from the C-band to the Ku-band (4-18 GHz) over an absorber thickness of 1.1-5.0 mm due to the efficient complementarities of complex permeability and permittivity resulting from the magnetic metal nanoparticles and lightweight carbon, as well as the particular particle/graphite core/shell microstructures in CNF-M. Moreover, a minimum reflection loss value of -67.5, -63.1, and -61.0 dB is achieved at 16.6, 12.9, and 13.1 GHz with a matching thickness of 1.3, 1.6, and 1.7 mm for CNF-Fe, CNF-Co, and CNF-Ni, respectively. These magnetic carbon nanofibers are attractive candidates for the new type of high performance EM-wave absorbing materials.